<生产厂家价格>

硅酸钙

硅酸钙用途

【用途一】
主要用作建筑材料、保温材料、耐火材料，涂料的体质颜料及载体
【用途二】
用作分析试剂及凝结剂
【用途三】
抗结剂;助滤剂;糖果抛光剂,胶母糖撒粉剂;大米涂层剂;悬浮剂.

硅酸钙名称

[ CAS 号 ]:
1344-95-2

[ 中文名 ]:
硅酸钙

[ 英文名 ]:
Calcium silicate

[英文别名 ]:

MFCD00015979
Calcium Silicate
dicalcium,silicate
EINECS 215-710-8
Silicic acid calcium salt

硅酸钙物理化学性质

[ 密度 ]:
2.9 g/mL at 25 °C(lit.)

[ 熔点 ]:
1540ºC

[ 分子式 ]:
CaO₃Si

[ 分子量 ]:
116.16

[ PSA ]:
92.24000

[ 外观性状 ]:
白色或奶油色粉末

[ 储存条件 ]:
库房通风低温干燥

[ 稳定性 ]:
Stable.

硅酸钙MSDS

详细MSDS(安全技术说明书)

硅酸钙毒性和生态

CHEMICAL IDENTIFICATION

RTECS NUMBER :: VV9150000

CHEMICAL NAME :: Silicic acid, calcium salt

CAS REGISTRY NUMBER :: 1344-95-2

LAST UPDATED :: 199712

硅酸钙安全信息

[ 个人防护装备 ]:
dust mask type N95 (US);Eyeshields;Gloves

[ 危害码 (欧洲) ]:
Xi

[ 风险声明 (欧洲) ]:
R36/37

[ 安全声明 (欧洲) ]:
S22-S26-S37/39

[ 危险品运输编码 ]:
NONH for all modes of transport

[ WGK德国 ]:
3

[ RTECS号 ]:
VV9170000

[ 海关编码 ]:
3824909990

硅酸钙制备

1.由氧化钙和二氧化硅在高温下煅烧熔融而成。

2.将纯石英与碳酸钙按CaO/SiO2为1∶1(摩尔比)混合，放入铂坩埚中于1500℃以上充分熔融后，将铂坩埚在水中急冷。将制得的偏硅酸钙玻璃体放入铂坩埚中，加热至800～1000℃，即开始结晶而生成βCaSiO3。

3.利用α-CaSiO3的冷却进行制备。

在纯固态下α-CaSiO3向β-CaSiO3转移是困难的，即使相当慢的冷却，也很难使转化进行。因此，往α-CaSiO3中加入其重量几分之一左右的偏钒酸钙Ca(VO3)2为助熔剂，在800～900℃时加热数日，用水和稀盐酸萃取除去钒酸盐，即可制得β-CaSiO3。

3.在氢氧化钙与硅胶按摩尔比为1∶1的混合物150～200mg中，加入5mL的电导水，用银内衬高压釜，在200℃下处理10日或在180℃下处理14日后，过滤，用丙酮洗涤，风干，就可制得石硅钙石(CaO·SiO2·16H2O)。如果将此化合物加热至800℃以上，即脱水而转化为β-CaSiO3。

硅酸钙海关

[ 海关编码 ]: 3824909990

硅酸钙文献

Tailored degradation of biocompatible poly(3-hydroxybutyrate-co-3-hydroxyvalerate)/calcium silicate/poly(lactide-co-glycolide) ternary composites: an in vitro study.

Mater. Sci. Eng. C. Mater. Biol. Appl. 33(7) , 4352-60, (2013)

Biodegradable materials, which are currently available for bone tissue regeneration, still have limitations regarding their degradation rate, mechanical stability and/or biological response. Thus, a n...

Study on analysis of waste edible oil with deterioration and removal of acid value, carbonyl value, and free fatty acid by a food additive (calcium silicate).

J. Oleo Sci. 62(2) , 109-14, (2013)

This study investigated the regeneration of waste edible oil using a food additive (calcium silicate, CAS). Waste edible oil was prepared by combined heat and aeration treatment. Moreover, the deterio...

Flue gas desulfurization gypsum and coal fly ash as basic components of prefabricated building materials.

Waste Manag. 33(3) , 628-33, (2013)

The manufacture of prefabricated building materials containing binding products such as ettringite (6CaO·Al2O3·3SO3·32H2O) and calcium silicate hydrate (CSH) can give, in addition to other well-define...