聚苯乙烯丁二烯共聚物

聚苯乙烯丁二烯共聚物用途

用于制造海绵橡胶、浸渍纤维和织物，还可直接用作胶粘剂、涂料等

用于铝塑复合管、无油密封、工具制造、圆珠笔握手套、汽车电器塑料件等

作胶姆糖基料，我国规定可用于胶姆糖，按生产需要适量使用。

用于食品着色。也用于羊毛、蚕丝、尼龙、皮革、纸张、塑料、木材、医药和化妆品的染色。
用于制造丁苯胶黏剂，也可与天然橡胶并用生产溶剂型压敏胶，还可
用于增黏SBS溶剂型胶黏剂。乳聚丁苯橡胶为通用型合成橡胶，能与其他合成橡胶混用，用于制造胶管、胶带、轮胎、胶布制品、鞋类、电线电缆、胶黏剂等。溶聚丁苯橡胶用于制造轮胎、输送带、胶管、模制品、胶布、胶鞋及医疗制品等。

聚苯乙烯丁二烯共聚物名称

[ CAS 号 ]:
9003-55-8

[ 中文名 ]:
聚(苯乙烯-co-丁二烯)

[ 英文名 ]:
polystyrene-b-polybutadiene-b-polystyrene

[中文别名 ]:

[英文别名 ]:

MFCD00134010
EINECS 618-370-2
Ethenylbenzenepolymer with 1,3-butadiene

聚苯乙烯丁二烯共聚物物理化学性质

[ 密度 ]:
1.04 g/mL at 25ºC

[ 沸点 ]:
145.2ºC at 760 mmHg

[ 熔点 ]:
-59ºC

[ 分子式 ]:
C₁₂H₁₄

[ 分子量 ]:
158.24000

[ 闪点 ]:
31.1ºC

[ 精确质量 ]:
158.11000

[ LogP ]:
3.68800

[ 外观性状 ]:
slab/chunk

[ 折射率 ]:
1.57

[ 储存条件 ]:
室温

[ 稳定性 ]:
Stable. Combustible. Incompatible with strong oxidizing agents.

[ 水溶解性 ]:
solvents with solubility parameters between 7.7 and 9.4: soluble

聚苯乙烯丁二烯共聚物MSDS

详细MSDS(安全技术说明书)

聚苯乙烯丁二烯共聚物毒性和生态

CHEMICAL IDENTIFICATION

RTECS NUMBER :: WL6478000

CHEMICAL NAME :: Styrene polymer with 1,3-butadiene

CAS REGISTRY NUMBER :: 9003-55-8

LAST UPDATED :: 199710

DATA ITEMS CITED :: 10

WISWESSER LINE NOTATION :: /*YR&1*/ &/*2U2*/

HEALTH HAZARD DATA

ACUTE TOXICITY DATA

TYPE OF TEST :: Standard Draize test

ROUTE OF EXPOSURE :: Administration into the eye

SPECIES OBSERVED :: Rodent - rabbit

REFERENCE :: 85JCAE "Prehled Prumyslove Toxikologie; Organicke Latky," Marhold, J., Prague, Czechoslovakia, Avicenum, 1986 Volume(issue)/page/year: -,1407,1986 *** REVIEWS *** IARC Cancer Review:Human No Adequate Data IMEMDT IARC Monographs on the Evaluation of Carcinogenic Risk of Chemicals to Man. (WHO Publications Centre USA, 49 Sheridan Ave., Albany, NY 12210) V.1- 1972- Volume(issue)/page/year: 19,231,1979 IARC Cancer Review:Animal No Adequate Data IMEMDT IARC Monographs on the Evaluation of Carcinogenic Risk of Chemicals to Man. (WHO Publications Centre USA, 49 Sheridan Ave., Albany, NY 12210) V.1- 1972- Volume(issue)/page/year: 19,231,1979 IARC Cancer Review:Group 3 IMSUDL IARC Monographs, Supplement. (WHO Publications Centre USA, 49 Sheridan Ave., Albany, NY 12210) No.1- 1979- Volume(issue)/page/year: 7,56,1987 *** NIOSH STANDARDS DEVELOPMENT AND SURVEILLANCE DATA *** NIOSH OCCUPATIONAL EXPOSURE SURVEY DATA : NOHS - National Occupational Hazard Survey (1974) NOHS Hazard Code - M2365 No. of Facilities: 7820 (estimated) No. of Industries: 77 No. of Occupations: 73 No. of Employees: 83064 (estimated) NOHS - National Occupational Hazard Survey (1974) NOHS Hazard Code - T1084 No. of Facilities: 621 (estimated) No. of Industries: 5 No. of Occupations: 7 No. of Employees: 10717 (estimated) NOHS - National Occupational Hazard Survey (1974) NOHS Hazard Code - T1682 No. of Facilities: 1331 (estimated) No. of Industries: 2 No. of Occupations: 4 No. of Employees: 7742 (estimated) NOES - National Occupational Exposure Survey (1983) NOES Hazard Code - X7643 No. of Facilities: 19175 (estimated) No. of Industries: 112 No. of Occupations: 101 No. of Employees: 314930 (estimated) No. of Female Employees: 52059 (estimated)

聚苯乙烯丁二烯共聚物安全信息

[ 个人防护装备 ]:
Eyeshields;Gloves;type N95 (US);type P1 (EN143) respirator filter

[ 危险品运输编码 ]:
NONH for all modes of transport

[ WGK德国 ]:
3

[ RTECS号 ]:
WL6478000

[ 海关编码 ]:
4002119000

聚苯乙烯丁二烯共聚物制备

(1) 由丁二烯和苯乙烯进行乳化共聚而得。用松香酸皂或脂肪酸皂为乳化剂，用过硫酸盐为催化剂，必要时，另加适宜的分子量调节剂和适宜的反应速度调节剂。由此所得者为液状胶乳。
如进一步在加热釜中(亦可同时加入其他食用级配料)进行凝聚，凝聚物经压榨除去浆液后，用加碱的(或不加碱的)热水进行洗涤，并用水淋洗，一直到成为中性。最后将凝聚体加以干燥，以除去可挥发性物质。此为由乳胶制成的固体状橡胶。75/25固体状橡胶亦可由丁二烯和苯乙烯在己烷溶液中用丁基锂为催化剂，进行溶体共聚而成。共聚后残存的溶剂和挥发性物质可用热水处理法或滚筒干燥法除去。
上述两种固体状橡胶的最后成品可制成板状或均一的可自由流动的颗粒。其中可含有食用级抗氧化剂。颗粒形式者，并可含有适当的分散剂。

(2) 用松香酸皂或脂肪酸皂为乳化剂，用过硫酸盐为引发剂，必要时添加适量的分子量调节剂和适宜的反应速度调节剂，由丁二烯与苯乙烯乳化共聚即得乳胶。
如进一步在加热釜内进行凝聚，凝聚物经压榨除去浆液后，先后用稀碱液和水洗至中性；最后将凝聚体干燥除去挥发性物质，即得固体橡胶。75/25固体橡胶也可由丁二烯和苯二烯在己烷中用丁基锂为催化剂，进行溶液共聚，再除去溶剂而得。

3.用松香酸皂或脂肪酸皂为乳化剂，以过硫酸盐为引发剂，由丁二烯与苯乙烯进行乳化共聚制得胶乳，再经凝聚、干燥得固体橡胶。75/25固体橡胶也可由丁二烯和苯二烯在己烷中用丁基锂为催化剂，进行溶液共聚制得。

4.工业上合成丁苯橡胶有乳液聚合法和溶液聚合法。乳液聚合又分高温工艺和低温工艺，其中，以低温乳液聚合使用较多。低温乳液聚合丁苯橡胶以丁二烯和苯乙烯为原料，以松香酸皂或脂肪酸皂等乳化剂在水中乳化，在引发剂作用下进行聚合:

将丁二烯、苯乙烯、乳化剂（如歧化松香皂）和水及碱混合成乳液，加入引发剂（如过氧化氢对孟烷或过氧化氢二异丙苯）、活化剂（如硫酸亚铁、EDTA或吊白块等）和调节剂（如叔十二硫醇等），在低温下（5～8℃）进行自由基共聚反应，反应达到预定的转化率时，加入终止剂（福美纳等），然后脱气、混合，加入稀硫酸和盐水凝聚，经过皂化、洗涤、真空吸滤，再次洗涤、粉碎、干燥即得成品。

溶聚丁苯橡胶是以丁二烯及苯乙烯为聚合单体，正丁基锂为引发剂，抽余油或环己烷为溶剂，四氢呋喃为结构调节剂，在聚合釜中进行间歇式无规共聚，聚合转化完成后，加入偶联剂进行偶合反应，然后经汽提水析凝聚，回收溶剂及四氢呋喃，含水胶粒经挤压脱水、膨胀干燥、压块包装后即为成品。

聚苯乙烯丁二烯共聚物海关

[ 海关编码 ]: 4002119000